Tubo d'acciaio senza saldatura A213
Ferriti senza saldatura e caldaie in acciaio legato austenitico, Super riscaldatore, e tubi per scambiatori di calore.
● Applicazione: per caldaia, Super riscaldatori, scambiatori di calore.
● Gamma di dimensioni: O.D.:12.7-114.3 mm W.T.: 1.65-10mm L.: 18000mm max.
In caso di domande,si prega di contattare sales@grandsteeltube.com
- Descrizione
- I vantaggi di Baosheng
- Indicazioni
- Inchiesta
ASTM A213 Alloy Seamless Steel Pipe
ASTM A213 covers seamless ferritic and austenitic steel boiler,Boiler Tube, and heat-exchanger tubes for high temperature services, designated Grades T5, TP304, and so on. Grades with letter H has highe creep-rupture strength compared with grades with no H. ASME SA213 seamless tubes are chrome moly Tubes with alloy element of chromium, molybdenum.
Grand supplies ASTM A213 Low Alloy Steel Tubes of all grades and dimensions. We also keep stock of ASTM A213 seamless tubes of Alloy Steel:T2, T11, T12, T22, T91, T92 in annealed and pickled, ricotto brillante, mill finish and polished conditions according to customer requirements
In caso di domande,sei più che benvenuto a contattare sales@grandsteeltube.com
1. Production of A213 seamless steel tubes since 2005.
2. Working with customers from West Asia,Nord America,America del Sud,ecc dal momento che 2006.
3. I campioni possono essere consegnati entro 25 giorni dopo la conferma
4. 40 giorni come periodo di produzione e consegna dopo la conferma dell'ordine.
5. 15,000 metri di tubi in acciaio senza saldatura in stock.
6. 200 le taglie possono essere offerte da OD:12.7mmxWT:1.65da mm a OD:114.3mmxWT:10millimetro
7. Ispezione di terze parti come:TUV,BV,SGS,ecc accettato
8. Il team di professionisti assiste le vostre esigenze speciali di tubi.
9. Altri tubi correlati:A179,A192,A213 seamless steel tube;and so on
In caso di domande,sei più che benvenuto a contattare sales@grandsteeltube.com
ASTM A213 Steel Tubes Outside Diameter and Wall Thickness Tolerance
OD, millimetro | Tolleranza OD |
---|---|
< 25.4 | +/- 0.10 |
25.4 – <= 38.1 | +/- 0.15 |
> 38.1 -< 50.8 | +/- 0.20 |
50.8 -< 63.5 | +/- 0.25 |
63.5 -< 76.2 | +/- 0.30 |
76.2 – <= 101.6 | +/- 0.38 |
> 101.6 – <= 190.5 | +0.38/-0.64 |
> 190.5 – <= 228.6 | +0.38/-1.14 |
OD, millimetro | WT Tolerance |
---|---|
<= 38.1 | +20%/-0 |
> 38.1 | +22%/-0 |
Table 1: Steel grade and chemical composition:
Grado d'acciaio | C | Mn | P | S | Si | Cr | Mo |
Max | Max | Max | Max | Max | Min | ||
T5 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.5 | 4.0-6.0 | 0.45-0.65 |
T9 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.25-1.00 | 8.0-10.0 | 0.90-1.10 |
T11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 1.0-1.50 | 0.44-0.65 |
T12 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 0.80-1.25 | 0.44-0.65 |
T21 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 2.65-3.35 | 0.80-1.06 |
T22 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 1.90-2.60 | 0.87-1.13 |
Table 2: Mechanical property:
Grado d'acciaio | Resistenza alla trazione | Snervamento | Allungamento | Durezza. Max | |
Min ksi(Mpa) | Min ksi(Mpa) | % | Brinell/Cickers | Rockwell | |
T5b | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC (Acciaio al collo) |
T9 | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC (Acciaio al collo) |
T12 | 60(415) | 32(220) | 30 | 163HBW/170HV | 85HRC (Acciaio al collo) |
T91 | 85(585) | 60(415) | 20 | 250HBW/265HV | 25HRC (Acciaio al collo) |
T92 | 90(620) | 64(440) | 20 | 250HBW/265HV | 25HRC (Acciaio al collo) |