Seamless Steel Tube A213
Seamless ferrites and austenitic alloy-steel boiler, super heater, and heat-exchangers tubes.
● Application: for boilers, super heaters, heat-exchangers.
● Size range: O.D.:12.7-114.3 mm W.T.: 1.65-10mm L.: 18000mm max.
Si tiene alguna pregunta,Por favor, póngase en contacto con sales@grandsteeltube.com
- Descripción
- Ventajas de Baosheng
- Características técnicas
- Indagación
ASTM A213 Alloy Seamless Steel Pipe
ASTM A213 covers seamless ferritic and austenitic steel boiler,Boiler Tube, and heat-exchanger tubes for high temperature services, designated Grades T5, TP304, etc. Grades with letter H has highe creep-rupture strength compared with grades with no H. ASME SA213 seamless tubes are chrome moly Tubes with alloy element of chromium, molybdenum.
Grand supplies ASTM A213 Low Alloy Steel Tubes of all grades and dimensions. We also keep stock of ASTM A213 seamless tubes of Alloy Steel:T2, T11, T12, T22, T91, T92 in annealed and pickled, recocido brillante, mill finish and polished conditions according to customer requirements
Si tiene alguna pregunta,Usted es más que bienvenido a contactar sales@grandsteeltube.com
1. Production of A213 seamless steel tubes since 2005.
2. Working with customers from West Asia,América del Norte,América del Sur,etc ya que 2006.
3. Las muestras se pueden entregar dentro de 25 días después de la confirmación
4. 40 días como el período de producción y la entrega después de la confirmación del pedido.
5. 15,000 metros de tubos de acero sin costura en stock.
6. 200 tamaños se pueden ofrecer desde OD:12.7mmxWT:1.65mm a OD:114.3mmxWT:10milímetro
7. Inspección de terceros como:TUV,BV,SGS,etc aceptado
8. El equipo profesional le ayuda a sus necesidades especiales de tubo.
9. Otros tubos relacionados:A179,A192,A213 seamless steel tube;etc
Si tiene alguna pregunta,Usted es más que bienvenido a contactar sales@grandsteeltube.com
ASTM A213 Steel Tubes Outside Diameter and Wall Thickness Tolerance
OD, milímetro | Tolerancia OD |
---|---|
< 25.4 | +/- 0.10 |
25.4 – <= 38.1 | +/- 0.15 |
> 38.1 -< 50.8 | +/- 0.20 |
50.8 -< 63.5 | +/- 0.25 |
63.5 -< 76.2 | +/- 0.30 |
76.2 – <= 101.6 | +/- 0.38 |
> 101.6 – <= 190.5 | +0.38/-0.64 |
> 190.5 – <= 228.6 | +0.38/-1.14 |
OD, milímetro | WT Tolerance |
---|---|
<= 38.1 | +20%/-0 |
> 38.1 | +22%/-0 |
Table 1: Steel grade and chemical composition:
Grado de acero | C | Mn | P | S | Si | Cr | Mo |
Máximo | Máximo | Máximo | Máximo | Máximo | Min | ||
T5 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.5 | 4.0-6.0 | 0.45-0.65 |
T9 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.25-1.00 | 8.0-10.0 | 0.90-1.10 |
T11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 1.0-1.50 | 0.44-0.65 |
T12 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 0.80-1.25 | 0.44-0.65 |
T21 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 2.65-3.35 | 0.80-1.06 |
T22 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 1.90-2.60 | 0.87-1.13 |
Table 2: Mechanical property:
Grado de acero | Tensile strength | Yield strength | Alargamiento | Dureza. Máximo | |
Min ksi(Mpa) | Min ksi(Mpa) | % | Brinell/Cickers | Rockwell | |
T5b | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC |
T9 | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC |
T12 | 60(415) | 32(220) | 30 | 163HBW/170HV | 85HRC |
T91 | 85(585) | 60(415) | 20 | 250HBW/265HV | 25HRC |
T92 | 90(620) | 64(440) | 20 | 250HBW/265HV | 25HRC |