100Tubo de acero para rodamientos Cr6

1. Relevant Steel Specification of 100Cr6 Bearing Steel

2. Chemical Composition of 100Cr6 Bearing Steel and Equivalents

3. Mechanical Propiedades of DIN 100Cr6 Bearing Steel

• 100Cr6 Steel Physical Properties

• DIN 100Cr6 Alloy Steel Thermal Properties

4. Forging of DIN 100Cr6 Bearing Steel

DIN 100Cr6 alloy steel is forged at 927 to 1205°C, and should not be forged below 925ºC. A post-forge equalization treatment is recommended at 745ºC for 4-6 hours followed by air cooling for SAE/AISI 52100 acero.

5. Heat Tratamiento for DIN 100Cr6 Bearing Steel

DIN 100Cr6 alloy bearing steel is heated at 816°C followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C followed by slowly cooling in order to reduce the machining stress.

Hot Working

DIN 100Cr6 bearing steels alloy can be hot worked at 205 to 538°C.

Cold Working

DIN 100Cr6 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.

Annealing

For spheroidize anneale, the following isothermal anneal is recommended:

• 1500ºF (815ºC) for 3 horas
• 1350ºF (735ºC) for 4 horas
• 1250ºF (675ºC) for 3 horas
• Slow cool to 1000ºF (540ºC) then air cool.

Quenching

DIN 100Cr6 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.

Tempering

Temper to desired hardness as indicated by tempering curves after water or oil quench.

The special steel grades for bearing steel pipe production include the following (G marked with “rolling”): chromium bearing steel such as GCr6, GCr9 (SiMn), GCrl5 (SiMn); Chromium free bearing steels such as GSiMnV (Re), GSiMnMoV (Re), GMnMoV (Re); Carburized bearing steel such as G20CrMo, G20Cr2Mn2Mo; High carbon chromium stainless bearing steel such as 9Cr18 (Mo), etc.

The smelting quality of bearing steel is required to be very high. It is necessary to strictly control the content of sulfur, phosphorus, hydrogen, etc., as well as the quantity, size and distribution of non-metallic inclusions and carbides. Because the quantity, size and distribution of non-metallic inclusions and carbides have a great impact on the service life of bearing steel, bearing failure is often caused by the propagation of microcracks around large inclusions or carbides.

The content of inclusions is closely related to the oxygen content in steel. The higher the oxygen content, the more inclusions and the shorter the service life. The larger the particle size and uneven distribution of inclusions and carbides are, the shorter their service life will be. Their size and distribution are closely related to the smelting process used and the smelting quality. The main processes for producing bearing steel are continuous casting and electric furnace smelting+electroslag remelting process smelting. A small number of processes such as vacuum induction+vacuum self consumption double vacuum or+multiple vacuum self consumption are used to improve the quality of bearing steel.