ASTM A213 Alloy Seamless Steel Pipe
ASTM A213 covers seamless ferritic and austenitic steel boiler,Boiler Tube, and heat-exchanger tubes for high temperature services, designated Grades T5, TP304, etc. Grades with letter H has highe creep-rupture strength compared with grades with no H. ASME SA213 seamless tubes are chrome moly Tubes with alloy element of chromium, molybdenum.
Grand supplies ASTM A213 Low Alloy Steel Tubes of all grades and dimensions. We also keep stock of ASTM A213 seamless tubes of Alloy Steel:T2, T11, T12, T22, T91, T92 in annealed and pickled, Recuit brillant, mill finish and polished conditions according to customer requirements
Si des questions,Vous êtes plus que bienvenu pour contacter sales@grandsteeltube.com
1. Production of A213 seamless steel tubes since 2005.
2. Working with customers from West Asia,Amérique du Nord,Amérique du Sud,etc depuis 2006.
3. Les échantillons peuvent être livrés dans les 25 jours après confirmation
4. 40 jours comme période de production et de livraison après confirmation de commande.
5. 15,000 meters of seamless steel tubes in stock.
6. 200 tailles peuvent être offertes à partir de OD:12.7mmxWT:1.65mm à OD:114.3mmxWT:10mm
7. Inspection par une tierce partie comme:TUV,BV,SGS,etc accepté
8. Une équipe professionnelle vous assiste dans vos besoins spéciaux en matière de tubes.
9. Autres tubes apparentés:A179,A192,A213 seamless steel tube;etc
Si des questions,Vous êtes plus que bienvenu pour contacter sales@grandsteeltube.com
ASTM A213 Steel Tubes Outside Diameter and Wall Thickness Tolerance
OD, mm | OD Tolerance |
---|---|
< 25.4 | +/- 0.10 |
25.4 – <= 38.1 | +/- 0.15 |
> 38.1 -< 50.8 | +/- 0.20 |
50.8 -< 63.5 | +/- 0.25 |
63.5 -< 76.2 | +/- 0.30 |
76.2 – <= 101.6 | +/- 0.38 |
> 101.6 – <= 190.5 | +0.38/-0.64 |
> 190.5 – <= 228.6 | +0.38/-1.14 |
OD, mm | WT Tolerance |
---|---|
<= 38.1 | +20%/-0 |
> 38.1 | +22%/-0 |
Table 1: Steel grade and chemical composition:
Nuance d’acier | C | Mn | P | S | Si | Cr | Lu |
Max | Max | Max | Max | Max | Min | ||
T5 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.5 | 4.0-6.0 | 0.45-0.65 |
T9 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.25-1.00 | 8.0-10.0 | 0.90-1.10 |
T11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 1.0-1.50 | 0.44-0.65 |
T12 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 0.80-1.25 | 0.44-0.65 |
T21 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 2.65-3.35 | 0.80-1.06 |
T22 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 1.90-2.60 | 0.87-1.13 |
Table 2: Mechanical property:
Nuance d’acier | Traction | Élasticité | Élongation | Dureté. Max | |
Min ksi(Mpa) | Min ksi(Mpa) | % | Brinell/Cickers | Rockwell | |
T5b | 60(415) | 30(205) | 30 | 179HBW/190HV | 89Le |
T9 | 60(415) | 30(205) | 30 | 179HBW/190HV | 89Le |
T12 | 60(415) | 32(220) | 30 | 163HBW/170HV | 85Le |
T91 | 85(585) | 60(415) | 20 | 250HBW/265HV | 25Le |
T92 | 90(620) | 64(440) | 20 | 250HBW/265HV | 25Le |