Nylon coated steel brake line tubes are used by many automakers. The tubes with nylon coating is also called NyGAL coated brake lines.

It is described in PA12 , with min coating thickness 100-200 μm, ASTM A875, followed by a topcoat of Nylon 11 or 12.

Appearance: The topcoat shall be uniform in color and free from discontinuities such as flow lines, pin holes, craters, or abnormal roughness. The topcoat shall be black in color unless otherwise specified on the engineering drawing

Film Thickness: The Nylon PA11 or PA12 topcoat shall have a min thickness of 150 μm, average thickness 170 μm.

Salt Spray Testing (Normal): 1000 hr min before white rust shows, dan 12000 hr min before red rust shows;

Salt Spray Testing (Gravel Impact): 2000 hr min before red rust.

Tabung nilon PA12 adalah tabung berlapis tembaga lapis ganda yang dilapisi dengan bahan organik PA12 (polydodecalactam) setelah pelapisan seng putih. Keuntungan terbesarnya adalah ketebalan lapisan lapisan nilon adalah 150 μ m -200 μ M, memastikan ketahanan korosi dan ketahanan aus yang kuat, dan waktu semprotan garam di atas 2000H. Sekarang banyak digunakan dalam pipa rem kendaraan, pipa power steering, pipa bahan bakar, Pasokan bahan bakar dan pipa balik.
Tabung nilon PA12, Bentuk umum adalah panjang lurus (200Mm–6000Mm) dan membentuk tabung (disesuaikan sesuai dengan kebutuhan pelanggan yang berbeda); Spesifikasi umum adalah φ 4.76*0.7、 φ 6*0.7、 φ 6.35*0.7、 φ 8 * 0.7, Spesifikasi lainnya dapat disesuaikan.

The relative density of PA12 is 1.02g/cm3, which is low in nylon products; Because of its low content of amide group, the water absorption is 0.25%, which is also low in nylon. The thermal decomposition temperature of PA12 is higher than 350 ℃, and the long-term use temperature is 80-90 ℃. PA12 membrane has good air tightness, and the water vapor transmission rate is 9g/m2. PA12 is resistant to alkali, minyak, yeast, inorganic diluted acid, aromatic hydrocarbon, dll. Therefore, PA12 is widely used in automobile pipeline system, such as multi-layer fuel pipeline system, vacuum brake booster pipe, hydraulic clutch pipe, central lubrication system pipe, dll. It can also be used for repairing inner tubes of industrial pipelines and contact expansion; Corrosive chemical industrial pipeline system. PA12 has good anti noise effect and is an ideal material for optical fiber sheath. It is also an excellent material for cable sheath to prevent termites and mice. The high toughness and strength of PA12 provide higher burst resistance pressure, which can be used as medium pressure natural gas transmission pipe. It has been applied in the United States, Western Europe and other countries. PA12 natural gas pipe can withstand higher working pressure and temperature than polyethylene (PE) pipe. PA12 natural gas transmission pipeline can withstand a pressure of 0.8~1.7MPa below 80 ℃, which can replace steel pipes within this range and is more competitive than polyolefin materials. PA12 is incompatible with most other plastic compounds. Even a small amount of other resin plastic pollution leads to turbid melt and finished parts. Therefore, before work, the plasticizing unit of the processing machine and all other melt channels should be cleaned very carefully. The materials of PA12 recycled materials must be free from foreign matters and dust particles, and the moisture content should be less than 0.1% by weight. A small amount of polymer, or even other polyamides, except for the same PA12 grade, will cause the corresponding molded parts to be turbid. If immediate post-treatment of waste is impossible, the gate or defective part shall be ground and stored in a moisture-proof bag, and it is necessary to reuse it after careful drying. The amount of recycled material added to the original PA12 material generally depends on some of the required properties, so the molded parts must be prepared by testing. If the end user’s requirements and specifications are allowed for the abrasive materials used, it is possible to add 25% of the recycled materials by weight. In some cases, such as thick wall profile extrusion, injection molded thick wall and high surface quality of optical elements or components, the particles should be dried in advance at any rate to prevent the formation of moisture streaks or uneven surfaces

Workshop kami,terletak di Changzhou,meliputi area seluas 13,000 meter persegi dilengkapi dengan fasilitas canggih untuk memproduksi tabung baja bundy dinding ganda dan tabung baja bundy dinding tunggal. Kapasitas produksi bulanan adalah 3,000,000 Meter.

Bahan-bahannya adalah :SPCC,SPHC,SPCE,BHG1, BHG2, materi lain dapat dicapai setelah diskusi.

Terutama ukuran adalah:4.76x0.70mm,6.35x0.70mm,8x0.70mm,9.53x0.70mm,10x0.70mm,12x0.70mm ukuran lain seperti:4.00x0.5mm,3.18x0.7mm,2.60x0.50mm juga diproduksi sesuai dengan ukuran.ukuran requirements.other dapat dicapai setelah diskusi.

1. Produksi tabung baja bundy dinding ganda & tabung baja bundy dinding tunggal sejak 2005.

2. Bekerja dengan pelanggan dari Eropa,Asia Barat,Amerika Selatan,sejak 2006dll

3. Sampel dapat dikirim dalam 10 hari setelah konfirmasi

4. 35 hari sebagai periode produksi dan pengiriman setelah konfirmasi pesanan.

5. 1,000,000 meter tabung baja bundy berlapis tembaga dalam stok.

6. Ukuran dapat ditawarkan dari OD:4.76mmxWT:0.5mm ke OD:12.7mmxWT:1.24Mm

7. Inspeksi pihak ketiga seperti:TUV,BV,SGS,dll diterima

8. Tim profesional membantu persyaratan tabung khusus Anda.

9. Tabung terkait lainnya dapat ditawarkan dengan harga yang kompetitif:Tabung Bundy Dinding Ganda Galvanis Putih / Kuning / Zaitun,PVF bundy tabung baja;dll

Kami telah mengirimkan tabung ini ke Peru,Prancis,Rusia,Korea Selatan untuk industri otomotif,sejak 2006.etc. Jika ada pertanyaan,Anda dipersilakan untuk menghubungi sales@grandsteeltube.com