ASTM A213 Alloy Seamless Steel Pipe
ASTM A213 covers seamless ferritic and austenitic steel boiler,Boiler Tube, and heat-exchanger tubes for high temperature services, designated Grades T5, TP304, jne. Grades with letter H has highe creep-rupture strength compared with grades with no H. ASME SA213 seamless tubes are chrome moly Tubes with alloy element of chromium, molybdenum.
Grand supplies ASTM A213 Low Alloy Steel Tubes of all grades and dimensions. We also keep stock of ASTM A213 seamless tubes of Alloy Steel:T2, T11, T12, T22, T91, T92 in annealed and pickled, kirkas hehkutettu, mill finish and polished conditions according to customer requirements
Jos sinulla on kysyttävää,olet enemmän kuin tervetullut ottamaan yhteyttä sales@grandsteeltube.com
1. Production of A213 seamless steel tubes since 2005.
2. Working with customers from West Asia,Pohjois-Amerikka,Etelä-Amerikka,jne koska 2006.
3. Näytteet voidaan toimittaa 25 päivää vahvistuksen jälkeen
4. 40 päivää tuotantojaksona ja toimitus tilausvahvistuksen jälkeen.
5. 15,000 metriä saumattomia teräsputkia varastossa.
6. 200 kokoja voidaan tarjota OD: ltä:12.7mmxWT:1.65mm - OD:114.3mmxWT:10mm
7. Kolmannen osapuolen tarkastus, kuten:TÜV,BV,SGS,jne hyväksytty
8. Ammattitaitoinen tiimi auttaa erityisiä putkivaatimuksiasi.
9. Muut samankaltaiset putket:A179,A192,A213 seamless steel tube;jne
Jos sinulla on kysyttävää,olet enemmän kuin tervetullut ottamaan yhteyttä sales@grandsteeltube.com
ASTM A213 Steel Tubes Outside Diameter and Wall Thickness Tolerance
OD, mm | OD-toleranssi |
---|---|
< 25.4 | +/- 0.10 |
25.4 – <= 38.1 | +/- 0.15 |
> 38.1 -< 50.8 | +/- 0.20 |
50.8 -< 63.5 | +/- 0.25 |
63.5 -< 76.2 | +/- 0.30 |
76.2 – <= 101.6 | +/- 0.38 |
> 101.6 – <= 190.5 | +0.38/-0.64 |
> 190.5 – <= 228.6 | +0.38/-1.14 |
OD, mm | WT Tolerance |
---|---|
<= 38.1 | +20%/-0 |
> 38.1 | +22%/-0 |
Table 1: Steel grade and chemical composition:
Teräslaatu | C | Mn | P | S | Si | Cr | Mo |
Max | Max | Max | Max | Max | Min | ||
T5 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.5 | 4.0-6.0 | 0.45-0.65 |
T9 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.25-1.00 | 8.0-10.0 | 0.90-1.10 |
T11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 1.0-1.50 | 0.44-0.65 |
T12 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 0.80-1.25 | 0.44-0.65 |
T21 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 2.65-3.35 | 0.80-1.06 |
T22 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 1.90-2.60 | 0.87-1.13 |
Table 2: Mechanical property:
Teräslaatu | Vetolujuus | Saannon vahvuus | Venymä | Kovuus. Max | |
Min ksi(Mpa) | Min ksi(Mpa) | % | Brinell/Cickers | Rockwell | |
T5b | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC |
T9 | 60(415) | 30(205) | 30 | 179HBW/190HV | 89HRC |
T12 | 60(415) | 32(220) | 30 | 163HBW/170HV | 85HRC |
T91 | 85(585) | 60(415) | 20 | 250HBW/265HV | 25HRC |
T92 | 90(620) | 64(440) | 20 | 250HBW/265HV | 25HRC |