Titanium coils
Because of the poor thermal conductivity of pure titanium, the emulsion with good lubrication effect and excellent cooling performance is required in the rolling process, and the rolling speed should not be too fast, in order to prevent the high temperature of pure titanium and cause the phenomenon of “sticking roller”, and “sticking roller” resulting in rough surface of titanium and poor quality. The residual water and oil on the surface of the titanium strip decompose during the annealing process, which affects the partial pressure of oxygen in the furnace and causes the decomposition reaction to go in the opposite direction, forming oxidation on the surface of the titanium strip and affecting the annealing quality. Because titanium strip annealing before full degreasing cleaning and drying plate surface. The degreasing speed of titanium strip is generally 20m/min, and the speed is adjusted according to the surface quality of the titanium strip after degreasing. Straightening is to ensure the flatness of the product plate.
- Priskribo
- Specifoj
- Enketo
Manufacturing process
Cold rolled titanium coil due to different production processes (or finished product surface) generally divided into cold rolled pickling surface titanium coil and cold rolled glossy titanium coil.
The manufacturing process of cold rolled pickling surface titanium coil of XRUN is: sponge titanium — melting — forging — hot rolling — heat treatment — shot blasting — hot rolled pickling white roll — cold rolling — heat treatment — shot blasting — pickling — edge cutting — inspection — cold rolled pickling white roll — packing and storage.
production process
In the production process, because the product is rolled twice, the oxide scale will be produced. Two heat treatment and shot blasting pickling are the treatment of the oxide scale on the surface of the product, so as to better ensure the quality of the product. Cold rolled pickling surface titanium coil is generally used in aerospace, industry and marine engineering. Compared with the former, cold rolled glossy titanium coil is more widely used. Similarly, there are two more steps in the production process of cold rolled titanium coil with glossy surface than pickling surface: degreasing annealing and straightening.
Because of the poor thermal conductivity of pure titanium, the emulsion with good lubrication effect and excellent cooling performance is required in the rolling process, and the rolling speed should not be too fast, in order to prevent the high temperature of pure titanium and cause the phenomenon of “sticking roller”, and “sticking roller” resulting in rough surface of titanium and poor quality. The residual water and oil on the surface of the titanium strip decompose during the annealing process, which affects the partial pressure of oxygen in the furnace and causes the decomposition reaction to go in the opposite direction, forming oxidation on the surface of the titanium strip and affecting the annealing quality. Because titanium strip annealing before full degreasing cleaning and drying plate surface. The degreasing speed of titanium strip is generally 20m/min, and the speed is adjusted according to the surface quality of the titanium strip after degreasing. Straightening is to ensure the flatness of the product plate.
Product parameters
Produkto | Specifo(mm} | Grado | Normo | Tensila Forto | Rendimento-Forto | Plilongigo |
pickling surface | Width(1.0~4.0) x (50~1200) x L | GR1/
GR2/ GR3/ GR4 |
ASTM B265 ASME SB265 |
≥240/
≥345/ ≥450/ ≥550 |
138~310/
275~450/ 380~550/ 483~655 |
≥24/
≥20/ ≥18/ ≥15 |
glossy surface | Width(0.2~3.0) x (50~1200) x L |
The titanium coil is mainly used as a container for heating and cooling. titanium coil fixation is divided into two kinds of detachable and non-detachable, This depends on the medium's corrosion of the titanium coil. But mainly based on removable type, convenient maintenance and cleaning of titanium coil.
Application features
Excellent corrosion resistance in many media
Smooth surface, clean layer
Malalta denseco, high strength and light weight
Malalta denseco, alta specifa forto
The density of metallic titanium is 4.51g/cm3, which is higher than that of aluminum and lower than that of steel, kupro, and nickel, but the specific strength is at the top of the metal.
Corrosion resistance
Titanium is a very active metal with a low equilibrium potential and a high tendency for thermodynamic corrosion in media. Tamen, titanium is actually very stable in many media. For example, titanium is resistant to corrosion in media such as oxidative, neutral and weak reducibility. This is because titanium and oxygen have a great affinity. In air or oxygen-containing medium, a dense, strong and inert oxide film is formed on the surface of titanium to protect the titanium matrix from corrosion. Even if it is due to mechanical wear, it will quickly heal or regenerate. This shows that titanium is a metal with a strong tendency to passivation. The oxide film of titanium below the temperature of 315°C always maintains this characteristic.
In order to improve the corrosion resistance of titanium, surface treatment technologies such as oxidation, electroplating, plasma spraying, ion nitriding, ion implantation, and laser processing have been studied. Titanium oxide film played a role in enhancing protection and obtaining desired corrosion resistance. A series of corrosion-resistant titanium alloys such as titanium-molybdenum, titanium-palladium, and titanium-molybdenum-nickel have been developed to meet the needs of metal materials in the production of sulfuric acid, hydrochloric acid, methylamine solution, high-temperature wet chlorine, and high-temperature chloride. Titanium-32-molybdenum alloys are used in titanium castings. Titanium-0.3 molybdenum-0.8 nickel alloys are used in environments where crevice corrosion or pitting corrosion frequently occurs. Titanium-0.2palladium alloys were used locally in titanium equipment, and good results were obtained.
Good heat resistance
The new titanium alloy can be used long-term at 600 °C or higher.
Low temperature resistance
Low temperature titanium alloy represented by titanium alloys TA7 (Ti-5Al-2.5Sn), TC4 (Ti-6Al-4V) and Ti-2.5Zr-1.5Mo, etc.Its strength increases with decreasing temperature, but the plasticity changes are not large.It maintains good ductility and toughness at -196-253°C and avoids cold brittleness. It is an ideal material for cryogenic vessels and tanks.
Strong anti-damping performance
After metal titanium is subjected to mechanical vibration and electric vibration, its own vibration decay time is the longest compared with steel and copper metal. The use of this property of titanium can be used as a tuning fork, a medical ultrasonic vibrator vibration element, and an advanced sound speaker vibration film.
Non-magnetic, ne-toksa
Titanium is a non-magnetic metal, it will not be magnetized in a large magnetic field, non-toxic and has good compatibility with human tissues and blood, so it is used by the medical community.
Tensile strength is close to its yield strength
This property of titanium shows that the yield strength ratio (tensile strength/yield strength) is high, indicating that the metal titanium material is poor in plastic deformation during forming. Since the ratio of the yield limit of titanium to the elastic modulus is large, the resilience of titanium when molded is large.
Good heat transfer performance
Although the thermal conductivity of titanium metal is lower than that of carbon steel and copper, due to the excellent corrosion resistance of titanium, the wall thickness can be greatly reduced, and the heat exchange mode between the surface and steam is droplet condensation, which reduces the thermal group. Titanium surface without scaling can also reduce the thermal resistance, so that the heat transfer performance of titanium is significantly improved.
Low modulus of elasticity
The modulus of elasticity of titanium is 106.4 GMPa at room temperature, which is only 57% of steel.
Suction performance
Titanium is a chemically very reactive metal that reacts with many elements and compounds at high temperatures. Titanium inhalation mainly refers to reaction with carbon, hydrogen, nitrogen, and oxygen at high temperatures.
Materialoj
Can be divided into: TA1 [Content 99,6], TA2 [Content 99,5], TA9 [Titanium Palladium Alloy], TA10 [Ti-Mo-Ni alloy
Titanium
The density of metallic titanium is 4.51g/cm3, which is higher than that of aluminum and lower than that of steel, kupro, and nickel, but the specific strength is at the top of the metal. Corrosion resistance, titanium is a very active metal, its equilibrium potential is very low, the tendency of thermodynamic corrosion in the medium. Tamen, titanium is actually very stable in many media. For example, titanium is resistant to corrosion in media such as oxidative, neutral and weak reducibility. This is because titanium and oxygen have a great affinity. In air or oxygen-containing medium, a dense, strong and inert oxide film is formed on the surface of titanium to protect the titanium matrix from corrosion. Even if it is due to mechanical wear, it will quickly heal or regenerate. This shows that titanium is a metal with a strong tendency to passivation. The oxide film of titanium below the temperature of 315°C always maintains this characteristic. In order to improve the corrosion resistance of titanium, surface treatment technologies such as oxidation, electroplating, plasma spraying, ion nitriding, ion implantation, and laser processing have been studied. Titanium oxide film played a role in enhancing protection and obtaining desired corrosion resistance. A series of corrosion-resistant titanium alloys such as titanium-molybdenum, titanium-palladium, and titanium-molybdenum-nickel have been developed for the production of sulfuric acid, hydrochloric acid, methylamine solution, high-temperature wet chlorine, and high-temperature chlorides, and for metal materials. Titanium castings use titanium-32 molybdenum alloys. Titanium-0.3 molybdenum-0.8 nickel alloys are used for crevice corrosion or pitting environments. Titanium-0.2 palladium alloys are used locally for titanium equipment. effect. Good heat resistance The new titanium alloy can be used long-term at 600°C or higher. Low-temperature-resistant titanium alloys such as titanium alloys TA7 (Ti-5Al-2.5Sn), TC4 (Ti-6Al-4V), and Ti-2.5Zr-1.5Mo, etc., whose low-temperature titanium alloys increase in strength as the temperature decreases, Plasticity is not great. It maintains good ductility and toughness at -196-253°C and avoids cold brittleness. It is an ideal material for cryogenic vessels and tanks.
Rilataj Produktoj
-
Legu pliRapida Vido
Stainless Steel Sheets
Stainless Steel Sheets & Plates are made up of austenitic steel mainly contain chromium and nickel with the addition of rare elements which offer high corrosion resistance, high tensile strength, excellent impact & toughness and high-temperature resistance at cryogenic temperatures. Moreover, these SS Sheets & Plates are highly demanded in various industries like chemical & nutraĵprilaborado, heat exchangers, fresh & saltwater marine environments, automobiles and more.
-
Legu pliRapida Vido
Copper Sheet
Copper sheet is a very workable and malleable form of metal, high in electrical and thermal conductivity, and provides excellent corrosion resistance. A beautiful and versatile metal, copper has been utilized for thousands of years. Historically, it served as a favorite choice in making tools, vessels, and sculptures. Copper is also known for its beautiful patinas. When exposed, unsealed, to an outdoor environment, copper begins to oxidize. This exposure creates beautiful color variations in the form of a patina. The coloring of the patina will change and develop character over time while serving to protect the metal from deterioration. People will also create a patina quickly with the use of chemical mixtures that speed the process up and allow a patina to develop without outdoor exposure. Copper sheets can also be hammered, tooled, or embossed for added texture and decorative or functional appeal and come in many thicknesses from very thin copper foil to thick copper plate. It also comes in many alloys that blend other metals with copper. At Grand Copper, we sell pure copper -C110 (other alloys and tempers available upon request). This high purity provides the premium quality needed for projects and applications in a wide range of industries and uses. We take pride in providing the best material. Our high-quality, affordable material and friendly, first-rate customer service have made us a leader in the industry for over a decade.
-
Legu pliRapida Vido
Copper Rod
Copper bar is a kind of non-ferrous metal processing bar, which has better processing performance and high conductivity. It is mainly divided into brass rod (copper zinc alloy, cheaper), purple copper rod (higher copper content).
Brass rod is a rod shaped object made of copper and zinc alloy, named for its yellow color. The melting point of brass, which contains 56% al 68% kupro, estas 934 al 967 gradoj. Brass has good mechanical properties and wear resistance, and can be used to manufacture precision instruments, ship parts, gun casings and so on. Used in air conditioning pipe, refrigerator pipe, oil pipe, water supply pipe and all kinds of mechanical materials, automotive synchronizer gear ring, Marine pump, valvo, structural parts, friction accessories, ktp.
Purple copper rod is named for its purple red color. It has good electric conductivity, heat conduction, corrosion resistance and processing properties. It can be welded and brazed. Characteristics: high purity, fine structure, low oxygen content. No porosity, trachoma, loose, excellent electrical conductivity, high precision of electroetching mold surface, after heat treatment process, no direction of the electrode, suitable for fine play, fine play, with good thermoelectric channel, processability, ductility, corrosion resistance and weather resistance.
-
Legu pliRapida Vido
Copper Strips
Copper strips have high electrical and thermal conductivity, that’s why copper strips are the best for transformer winding.
What’s more, copper strips transfer heat more effectively than other metals strips.
Copper strips are more malleable and have high tensile strength. Corrosion resistance, high degree stability, and heat dissipation of copper strips are superior to other metals.
Copper strips are mostly used in the electrical and electronics sectors because copper is non-magnetic and non-sparking. Copper strips are mostly used in heat exchangers, transformers winding, condensers, and lightning conductors.
Copper strip thickness range from 0.03mm to 3.0mm. Copper strips can be manufactured in different widths and thicknesses per the customer’s requirement.
Se ajnaj demandoj, bonvolu bonvolu kontakti sales@grandsteeltube.com
-
Legu pliRapida Vido
Aluminium Coil
Aluminium coil is a rolled product, produced in a coiled form of a continuous strip, and has an inner diameter and outer diameter. ID from50mm to 1000mm. Aluminium alloy grade including 1xxx, 2xxx, 3xxx, 4xxx, 5xxx, 6xxx, 7xxx, 8xxx. But the most common is 1050, 3003, 6061 kaj 5251 aluminum coil. Thickness from 0.045-80mm, width from 60-2650mm. Common widths of aluminum coil is 800mm,1000mm, 1250mm,1450mm and 1500mm.
Multiple industries rely on aluminium coils for a variety of applications, such as automotive, construction, heat transfer, pharmaceutical, electrical, and food industry. Compared to other materials, aluminum is a far superior material in many instances. Aluminum coil can be supplied with standard mill finish, or it can be brushed, checkered, color coated, satin-finished and anodized. Aluminium sheet or aluminium foil can be cut into coils as per client’s requirements.
-
Legu pliRapida Vido
Brass Bar
-
Legu pliRapida Vido
Copper Coils
It may seem that a copper coil is a simple piece of coiled wire that can be wound and put to use. As with any form of industrial product, copper coils have to be precisely engineered to fit an application. The winding process has to be completed with precision to ensure the proper distance between the wires and the diameter of the opening.
Each product that uses copper coils requires that a certain number of turns be made to provide the correct amount of resistance. Inaccurate calculations can lead to inefficiency and possible failure of the coil or device. For this reason, the engineers at Metal Associates guarantee that they have closely examined the specification of an application such that the diameter, spacing, wire thickness, and number of turns exactly matches the design of the product where the copper coil will be used.
-
Legu pliRapida Vido
Stainless Steel Foil
Stainless steel foils are thin strips of stainless steel that are less than 0.2 mm in thickness and less than 300 mm in width.
Stainless steel foils offer a variety of advantages, including chemical stability, high strength-to-weight ratio, electrical insulation and corrosion resistance.
Stainless steel foil is used in the production of heat exchangers, capacitors and fuel cells; as well as in medical equipment and food processing machinery.
Stainless steel foils are a versatile material with many advantages. Its high corrosion resistance, good thermal and electrical conductivities and its ductility makes it an excellent choice for a wide range of applications.
Stainless steel foil is available in several different grades. These include austenitic series, ferritic series, martensitic series, duplex and super duplex series. Each grade has different alloying elements that contribute to the properties of the foil.
The most common grades of stainless steel foils are 304 kaj 316. These grades are supplied in thicknesses ranging from 0.009mm to 0.3mm. Other grades of stainless steel foil are also available upon request including 409, 430 and duplex 2205.
-
Legu pliRapida Vido
Stainless Steel Coil
Stainless steel coil can be divided into cold rolled stainless steel coil and hot rolled stainless steel coil according to different production processes.
According to the materials, they can be divided into austenite, martensite, ferrite and duplex.
Common use stainless steel coils grades are often represented by digital symbols.
There are 200 serio, 300 serio, 400 series and duplex series.
304, 304L, 316 and 316L stainless steel coils are the most popular and economical grades of stainless steels.
Stainless steel 304/304L coils and stainless steel 316/316L coils, along with duplex stainless steel coils offer good corrosion resistance to many chemical environments as well as marine and industrial exposures.
-
Legu pliRapida Vido
Titanium Bar
- DIN2391 Preciza Ŝtala Tubo
- EN10305-1/4 Preciza Ŝtala Tubo
- EN10305-2/3/5/6 Precizaj Tuboj
- SAE-Serio Precizecaj Tuboj
- ISO8535-1 Fuel Injection Tube
- Single/Doulbe Wall Bundy Tube
- Kaldrono & Premŝtalaj Tuboj
- Senjunta Honed/SRB Ŝtala Tubo
- Neoksideblaj Kapilaraj Ŝtalaj Tuboj
- Senjuntaj Neoksideblaj Tuboj & Pipoj
- Velditaj Neoksideblaj Tuboj & Pipoj
- Injekto & Kontrolliniaj Tuboj
- Nikelaj Alojaj Tuboj & Pipoj
- Neferaj Kapilaraj Tuboj
- Aluminiaj Tuboj & Pipoj
- Latunaj Tuboj & Pipoj
- Kupro Tuboj & Pipoj
- Titanaj Tuboj & Pipoj
- Ekstrudita/Veldita Naĝilo-Tubo
- Ne-Ferra Preciza Tubo
- Specialformaj Ŝtalaj Tuboj
- Metala Bobeno / Folio / Folio / Strio