Νάιλον επίστρωση Bundy σωλήνα

Nylon coated steel brake line tubes are used by many automakers. The tubes with nylon coating is also called NyGAL coated brake lines.

It is described in PA12 , with min coating thickness 100-200 μm, ASTM A875, followed by a topcoat of Nylon 11 ή 12.

Εμφάνιση: The topcoat shall be uniform in color and free from discontinuities such as flow lines, pin holes, craters, or abnormal roughness. The topcoat shall be black in color unless otherwise specified on the engineering drawing

Film Thickness: The Nylon PA11 or PA12 topcoat shall have a min thickness of 150 μm, average thickness 170 μm.

Salt Spray Testing (Normal): 1000 hr min before white rust shows, και 12000 hr min before red rust shows;

Salt Spray Testing (Gravel Impact): 2000 hr min before red rust.

Ο νάιλον σωλήνας PA12 είναι ένας επιχρυσωμένος σωλήνας διπλής στρώσης επικαλυμμένος με οργανικό υλικό PA12 (πολυδωδεκαλακτάμη) μετά από λευκή επιψευδαρσωμάτωση. Το μεγαλύτερο πλεονέκτημά του είναι ότι το πάχος επικάλυψης του νάιλον στρώματος είναι 150 μ μ -200 μ Μ, εξασφαλίζοντας την ισχυρή αντοχή του στη διάβρωση και τη φθορά, και ο χρόνος ψεκασμού αλατιού είναι πάνω από 2000H. Τώρα χρησιμοποιείται ευρέως στον αγωγό φρένων οχημάτων, αγωγός υδραυλικού τιμονιού, αγωγός καυσίμων, αγωγός τροφοδοσίας και επιστροφής καυσίμων.
Σωλήνας νάιλον PA12, Οι κοινές μορφές έχουν ευθύ μήκος (200χιλ.–6000χιλ.) και σχηματισμένο σωλήνα (προσαρμοσμένο σύμφωνα με τις διαφορετικές ανάγκες των πελατών); Οι κοινές προδιαγραφές είναι φ 4.76*0.7、 φ 6*0.7、 φ 6.35*0.7、 φ 8 * 0.7, Άλλες προδιαγραφές μπορούν να προσαρμοστούν.

The relative density of PA12 is 1.02g/cm3, which is low in nylon products; Because of its low content of amide group, the water absorption is 0.25%, which is also low in nylon. The thermal decomposition temperature of PA12 is higher than 350 °C, and the long-term use temperature is 80-90 °C. PA12 membrane has good air tightness, and the water vapor transmission rate is 9g/m2. PA12 is resistant to alkali, λάδι, yeast, inorganic diluted acid, aromatic hydrocarbon, κλπ. Therefore, PA12 is widely used in automobile pipeline system, such as multi-layer fuel pipeline system, vacuum brake booster pipe, hydraulic clutch pipe, central lubrication system pipe, κλπ. It can also be used for repairing inner tubes of industrial pipelines and contact expansion; Corrosive chemical industrial pipeline system. PA12 has good anti noise effect and is an ideal material for optical fiber sheath. It is also an excellent material for cable sheath to prevent termites and mice. The high toughness and strength of PA12 provide higher burst resistance pressure, which can be used as medium pressure natural gas transmission pipe. It has been applied in the United States, Western Europe and other countries. PA12 natural gas pipe can withstand higher working pressure and temperature than polyethylene (PE) pipe. PA12 natural gas transmission pipeline can withstand a pressure of 0.8~1.7MPa below 80 °C, which can replace steel pipes within this range and is more competitive than polyolefin materials. PA12 is incompatible with most other plastic compounds. Even a small amount of other resin plastic pollution leads to turbid melt and finished parts. Therefore, before work, the plasticizing unit of the processing machine and all other melt channels should be cleaned very carefully. The materials of PA12 recycled materials must be free from foreign matters and dust particles, and the moisture content should be less than 0.1% by weight. A small amount of polymer, or even other polyamides, except for the same PA12 grade, will cause the corresponding molded parts to be turbid. If immediate post-treatment of waste is impossible, the gate or defective part shall be ground and stored in a moisture-proof bag, and it is necessary to reuse it after careful drying. The amount of recycled material added to the original PA12 material generally depends on some of the required properties, so the molded parts must be prepared by testing. If the end user’s requirements and specifications are allowed for the abrasive materials used, it is possible to add 25% of the recycled materials by weight. In some cases, such as thick wall profile extrusion, injection molded thick wall and high surface quality of optical elements or components, the particles should be dried in advance at any rate to prevent the formation of moisture streaks or uneven surfaces

Το εργαστήρι μας,που βρίσκεται σε Changzhou,καλύπτει έκταση 13,000 square meters equipped with the state-of-art facilities to manufacture the double wall bundy steel tubes and single wall bundy steel tubes .The monthly production capacity is 3,000,000 Μέτρα.

Τα υλικά είναι: :SPCC,SPHC,SPCE,BHG1, BHG2, άλλα υλικά μπορούν να επιτευχθούν μετά από συζήτηση.

Κυρίως τα μεγέθη είναι::4.76x0.70mm,6.35x0.70mm,8x0.70mm,9.53x0.70mm,10x0.70mm,12x0.70mm other size like:4.00x0.5mm,3.18x0.7mm,2.60x0.50mm is also produced according the requirements.other sizes can be achieved after discussion.

1. Production of double wall bundy steel tubes & single wall bundy steel tubes since 2005.

2. Συνεργασία με πελάτες από την Ευρώπη,Δυτική Ασία,Νότια Αμερική,since 2006etc

3. Τα δείγματα μπορούν να παραδοθούν εντός 10 ημέρες μετά την επιβεβαίωση

4. 35 ημέρες ως περίοδος παραγωγής και παράδοση μετά την επιβεβαίωση της παραγγελίας.

5. 1,000,000 meters of copper coated bundy steel tube in stock.

6. Τα μεγέθη μπορούν να προσφερθούν από την OD:4.76μμxΒΤ:0.5mm έως OD:12.7μμxΒΤ:1.24χιλ.

7. Επιθεώρηση τρίτου μέρους όπως:ΤΟΥΒ,ΒΔ,ΥΓ.,κλπ αποδεκτό

8. Η επαγγελματική ομάδα βοηθά τις ειδικές απαιτήσεις σωλήνων σας.

9. Άλλοι σχετικοί σωλήνες μπορούν να προσφερθούν με ανταγωνιστικές τιμές:white/yellow/olive green galvanized double wall bundy tubes,PVF bundy steel tubes;κλπ

Έχουμε παραδώσει αυτούς τους σωλήνες στο Περού,Γαλλία,Ρωσία,Νότια Κορέα για την αυτοκινητοβιομηχανία,since 2006.etc.If any questions,είστε περισσότερο από ευπρόσδεκτοι να επικοινωνήσετε sales@grandsteeltube.com